Slickote M1 Air Dry Solid Film Lubricant
Apply in accordance with Mil-PRF-46147C Ty1 & 2 /Lead Free /Low VOC
Slickote M1 is an air cured, low voc resin bonded solid film
lubricant coating which meets the requirements of Mil-PRF-46147C Ty 1 and 2.
reduce wear and prevent galling, corrosion and seizure of metals.
Where conventional lubricants are difficult to apply or retain, or where
other lubricants may be easily
For sliding motion applications such as plain and spherical bearings, flap tracks, hinges, threads and cam surfaces.
temperature ranges are from -67 deg
C to 93 deg C (-88 deg F to 200 deg F)
mechanisms are operated at infrequent intervals or are lubricated for life.
long term corrosion protection is required under static conditions.
Where extremely heavy loaded lubrication is required including initial start up of heavy loaded mechanisms designed for fluid lubrication.
touch up to worn surfaces previously coated with solid film lubrication
Metal Preparation: All surfaces must be thoroughly cleaned, degreased,
free of rust, oxides or other surface
Aluminum – Anodize and seal iaw Mil-A-8625, type II, Class 1
Steel – Abrasive clean (180 to 220 grit aluminum oxide) and
phosphate coat iaw DOD-P-16232 type M or Z,
Stainless Steel - Abrasive clean (120 grit aluminum oxide)
and Passivate iaw AMS QQ-P-35.
Titanium – Abrasive Clean
(180 to 220 grit aluminum oxide) and alkaline anodize.
Mix well, in mechanical paint shaker
Concentrate only: Reduce with SlicKote Reducer 1:1 (or 50/50 mix of Acetone
& Oxsol 100 by Wt)
3) Apply with spray gun, brushing or dipping:
to .008 mm to .013 mm coating
thickness (.0002 to .0005 inch)
Air dry for 30 minutes
#1 Grey (natural), #2
Concentrate: Reduce with SlicKote Reducer 2:1 by
volume (or 50% Acetone/ Oxsol100)
Ambient (< 90 degF)
Air Dry 18 Hours
Shelf Life: 1 year from date of manufacture
Store in closed container
Zahn #1, 30 sec
not use in food processing or handling equipment or surfaces with food contact.
Use only in well ventilated area or hood where no flames or other ignition
sources are present.
Solvent base, air dried resin bonded coating based on
Uses exempt solvents to achieve low voc, <135 g/l
(meets both type 1 and 2 requirements)
Lead and Graphite Free
Used to provide a thin coating with exceptional
protection aganist wear and corrosion.
Operating temp range: -88 deg F to +200 deg F
.0002 to .0005 inch
Tested in accordance with Mil-PRF-46147
ASTM B-117, >100 Hr
*Mil-PRF-7808, Aircraft Turbine Oil
*SAE J1966 gd50, Aircraft Oil
*Mil-PRF-372, Cleaning Cmpd
*ASTM D-1193, Reagent Water
*Mil-H-46170, Hydraulic Fluid
*Mil-L-PRF-32033, Lube Oil
*VV-D-1078, Silicone Fluid
*Mil-L-14107, Weapon Lube Oil
*Mil-L-46000, Semi Fluid Lubricant
*Mil-L-63460, Cleaner & Preserve
ASTM D-2625A, Endurance Life >120 min
ASTM D-2625B, Load Capacity >250 Lbf